corrosion cracking的例句大全

High environment humidity increases the susceptibility to hy-drogen induced cracking and stress corrosion cracking.

高湿度能增大氢致裂纹和应力腐蚀开裂倾向.

This offers a practical e example that chlorine ion caused stress corrosion cracking of brass.

为氯离子引起黄铜应力腐蚀开裂提供了实例.

The results show that the fibre orientation affects on the stress corrosion cracking of GRP seriously.

结果表明,纤维取向对玻璃纤维增强塑料的应力腐蚀行为有很大影响.

The reason, influence coefficient and control measure of the corrosion cracking were disserted in this article.

本文详细论述了不锈钢波形膨胀节腐蚀破裂的原因 、 影响因素及控制措施.

Its shortcomings are mainly low structural stability, low low-frequency fatigue strength and stress corrosion cracking.

其缺点是组织稳定性不好 、 低频疲劳强度低、有应力腐蚀开裂倾向.

Preferential corrosion cracking at or along the grain boundaries of a metal.

优先腐裂或沿着金属晶界发生的腐蚀.

Laser shock processing ( LSP ); Mg alloy; Residual stress; Stress corrosion cracking SCC.

激光冲击强化; 镁合金; 残余应力; 应力腐蚀开裂.

It also has an excellent resistance to pitting and to stress-corrosion cracking.

它还具有优良的耐点蚀和应力腐蚀开裂.

It is shown that the surface cracking is caused by the stress corrosion cracking.

结果表明,该表面开裂为应力腐蚀开裂.

Stress corrosion cracking in which the cracking occurs along grain boundaries.

沿着晶界发生的应力腐蚀开裂.

Breakage mechanism of these pipes is tipping corrosion, accompanied with intergranular corrosion and stress corrosion cracking.

腐蚀机理一般为点蚀, 往往伴随晶间腐蚀和应力腐蚀.

With increasing corrosion time the impact toughness of high Mn steel obviously decreased. The major mechanism was effect of the caustic embrittlement cracking.

随着热强碱腐蚀时间的延长，高锰钢的冲击韧度明显降低，碱脆开裂是造成高锰钢冲击韧度下降的主要原因。

Analysis on stress corrosion cracking of layer plates in initiating explosion location of Pingyin's urea reactor

平阴尿素合成塔起爆源处层板应力腐蚀开裂分析

Stress corrosion cracking of a high strength prestressing steel wire in saturated ca ( oh)_2+ nacl solutions

高强度预应力钢丝在饱和Ca（OH）2+NaCl环境中的应力腐蚀开裂

Evaluation for sulfide stress corrosion cracking of cold-high pressure segregator

冷高压分离器在H2S环境下应力腐蚀开裂敏感性评估

The process equipments and pipelines of atomospheric vacuum, catalytic cracking and coking unit etc. of changling refined and chemical company are suffered from serious corrosion caused by mixed refining foreign high sulphur bearing crude.

长岭炼化公司因掺炼国外高含硫原油，常减压、催化裂化、焦化等装置的工艺设备和管道遭受到较严重腐蚀。

The Corrosion Cracking and Protection of the Ammonium Carbamate Pump Cylinder

氨基甲酸铵泵泵体的腐蚀开裂与防护

Study on Corrosion Cracking of Bellows Expansion Joint Made of Stainless Steel

对真空制盐车间不锈钢膨胀节热影响区腐蚀裂纹的探讨

An aeration device for hydrogen sulfide for sulfide stress corrosion cracking test

H2S应力腐蚀试验用H2S气通设计

An Investigation on Interface Reaction Regularity for Caustic Stress Corrosion Cracking of Fe-Cr-Ni Alloy

Fe-Cr-Ni合金碱性应力腐蚀破裂界面反应规律的研究